Semitron Static Dissipative Acetal…
| Mechanical | ASTM Test Method | Value | Units |
|---|---|---|---|
| Strength to Weight Ratio | - | 4.1 | ksi |
| Specific Gravity @73 F | D792 | 1.33 | - |
| Tensile Strength @73 F, (ult)/(yld) | D638 | 5,400 (ult) | psi |
| Tensile Modulus of Elasticity @73 F | D638 | 200,000 | psi |
| Tensile Elongation at Break @73 F | D638 | 15 | % |
| Flexural Strength @73 F | D790 | 7,300 | psi |
| Flexural Modulus of Elasticity @73 F | D790 | 220,000 | psi |
| Shear Strength @73 F | D732 | - | psi |
| Comprehensive Strength, (% Deformation) @73 F | D695 | 8,000 (10) | psi |
| Comprehensive Modulus of Elasticity @73 F | D695 | 175,000 | psi |
| Hardness, Rockwell, Scale as noted @73 F | D785 | M50 (R108) | - |
| Hardness, Durometer, Shore D @73 F | D2240 | - | - |
| Izod Impact, (Notched) @73 F | D256 Type A | 1.5 | ft-lb/in of notch |
| Coefficient of Friction, (Dry vs Steel) Dynamic | - | 0.29 | - |
| Limiting PV, (with 4 to 1 factor of safety applied) | - | 2,200 | psi-ft/min |
| Thermal | ASTM Test Method | Value | Units |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion @73 F | E-831 (TMA) | 9.3 E-05 | in/in/F |
| Heat Deflection Temperature @264 psi | D648 | 225 | F |
| Tg-Glass transition termperature, (Amorphous) | D3418 | - | F |
| Melting Point, (VS=Vicat Softening Temp.) | D3418 | 320 | F |
| Continuous Service Temperature in Air, (Max.) | - | 180 | F |
| Thermal Conductivity | - | - | BTU-in/hr-ft2-F |
| Electric | ASTM Test Method | Value | Units |
|---|---|---|---|
| Dielectric Strength, Short Term | D149 | - | Volts/mil |
| Volume Resistivity | D257 | 1E11 - 1E12 | ohm-cm |
| Dielectric Constant @10E6 Hz | D150 | - | - |
| Dissipation Factor @10E6 Hz | D150 | - | - |
| Flammability @3.1 mm unless noted | UL94 | HB | - |
| H2O | ASTM Test Method | Value | Units |
|---|---|---|---|
| Water Absorption, Immersion, 24 hours | D570(7) | 2.0 | % by weight |
| Water Absorption, Saturation | D570(7) | 7.20 | % by weight |